Compositional and strain analysis of In(Ga)N/GaN short period superlattices

GP Dimitrakopulos and IG Vasileiadis and C Bazioti and J Smalc- Koziorowska and S Kret and E Dimakis and N Florini and T Kehagias and T Suski and T Karakostas and TD Moustakas and P Komninou, JOURNAL OF APPLIED PHYSICS, 123, 024304 (2018).

DOI: 10.1063/1.5009060

Extensive high resolution transmission and scanning transmission electron microscopy observations were performed in In(Ga)N/GaN multi- quantum well short period superlattices comprising two-dimensional quantum wells (QWs) of nominal thicknesses 1, 2, and 4 monolayers (MLs) in order to obtain a correlation between their average composition, geometry, and strain. The high angle annular dark field Z-contrast observations were quantified for such layers, regarding the indium content of the QWs, and were correlated to their strain state using peak finding and geometrical phase analysis. Image simulations taking into thorough account the experimental imaging conditions were employed in order to associate the observed Z-contrast to the indium content. Energetically relaxed supercells calculated with a Tersoff empirical interatomic potential were used as the input for such simulations. We found a deviation from the tetragonal distortion prescribed by continuum elasticity for thin films, i.e., the strain in the relaxed cells was lower than expected for the case of 1 ML QWs. In all samples, the QW thickness and strain were confined in up to 2 ML with possible indium enrichment of the immediately abutting MLs. The average composition of the QWs was quantified in the form of alloy content. Published by AIP Publishing.

Return to Publications page