Interaction of Edge Dislocations with Graphene Nanosheets in Graphene/Fe Composites

L Wang and JF Jin and JY Cao and PJ Yang and Q Peng, CRYSTALS, 8, 160 (2018).

DOI: 10.3390/cryst8040160

Graphene is an ideal reinforcement material for metal-matrix composites owing to its exceptional mechanical properties. However, as a 2D layered material, graphene shows highly anisotropic behavior, which greatly affects the mechanical properties of graphene-based composites. In this study, the interaction between an edge dislocation (b = 1/2 (111)) and a pair of graphene nanosheets (GNSs) in GNS reinforced iron matrix composite (GNS/Fe) was investigated using molecular dynamic simulations under simple shearing conditions. We studied the cases wherein the GNS pair was parallel to the 1(1) over bar 0,11(2) over bar, and (111) planes, respectively. The results showed that the GNS reinforcement can effectively hinder dislocation motion, which improves the yield strength. The interaction between the edge dislocation and the GNS pair parallel to the 11(2) over bar plane showed the strongest effect of blocking dislocations among the three cases, resulting in increases in the shear modulus and yield stress of 107% and 1400%, respectively. This remarkable enhancement was attributed to the Orowan "by-passing" strengthening mechanism, whereas cross-slip of dislocation segments was observed during looping around GNSs. Our results might contribute to the development of high-strength iron matrix composites.

Return to Publications page