Flow strength limit of nanocrystalline tantalum predicted with molecular dynamics simulations

C Huang and XH Peng and YB Zhao and SY Weng and B Yang and T Fu, MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 738, 1-9 (2018).

DOI: 10.1016/j.msea.2018.09.053

The effects of grain size (d) on the flow strength (sigma(flow)) as well as the deformation mechanism of nanocrystalline tantalum (NC-Ta) under uniaxial tension were investigated with molecular dynamics (MD) simulations. It showed that there exists a critical grain size of d(cr )= 7 nm, at which a sigma(flow) reaches the maximum. Generalized stacking fault energy curves suggest that < 111 > 110 and < 111 > 112 are the easiest slip systems for dislocations and twins to occur, and after that the other slip systems might be activated. The twinning mechanism of Ta crystal is analyzed to understand the plastic deformation. For the sample with d > 7 nm, the variation of sigma(flow) against d follows the Hall-Petch relationship, attributed to the strengthening due to the accumulations of dislocations and twins with the decrease of d. For the sample with d < 7 nm, the variation of a sigma(flow) against d exhibits an inverse Hall-Petch relationship, attributed to the softening induced by grain boundary activities. Additionally, cracks can be found in the samples with larger d, but they do not significantly propagate and affect the flow stress. Our simulation results could be beneficial to the design and optimization of such kind of high-performance nano-structured materials.

Return to Publications page