Vacancy-Induced Thermal Transport and Tensile Mechanical Behavior of BeO

ASMJ Islam and MS Islam and NZ Mim and MS Akbar and MS Hasan and MR Islam and C Stampfl and J Park, ACS OMEGA, 7 (2022).

DOI: 10.1021/acsomega.1c06491

Because of the rapid shrinking trend of integrated circuits, the performances of nanodevices and nanomechanical systems are greatly affected by the joule heating and mechanical failure dilemma. In addition, structural defects are inevitable during experimental synthesis of nanomaterials, which may alter their physical properties significantly. Investigation of the thermal transport and mechanical behavior of nanostructured materials with structural defects is thus a crucial requirement. In this study, the thermal conductivity (TC) and tensile mechanical behavior of monolayer honeycomb BeO are systematically explored using molecular dynamics simulations. An infinite length bulk TC of similar to 277.77 +/- 8.93 W/mK was found for the pristine monolayer BeO. However, the insertion of 1% single vacancy (SV) and double vacancy (DV) defects reduces the TC by similar to 36.98 and similar to 33.52%, respectively. On the other hand, the uniaxial tensile loading produces asymmetrical fracture stress, elastic modulus, and fracture strain behaviors in the armchair and zigzag directions. The elastic modulus was reduced by similar to 4.7 and similar to 6.6% for similar to 1% SV defects along the armchair and zigzag directions, respectively, whereas the reduction was similar to 2.7 and similar to 5.1% for similar to 1% DV defects. Moreover, because of the strong symmetry-breaking effect, both the TC and mechanical strength were significantly lower for the SV defects than those for the DV defects. The highly softening and decreasing trends of the phonon modes with increasing vacancy concentration and temperature, respectively, were noticed for both types of defects, resulting in a reduction of the TC of the defected structures. These findings will be helpful for the understanding of the heat transport and mechanical characteristics of monolayer BeO as well as provide guidance for the design and control of BeO-based nanoelectronic and nanoelectromechanical devices.

Return to Publications page