Morphology and Dynamics in Hydroxide-Conducting Polysulfones

AL Frischknecht and PJI' Veld and IV Kolesnichenko and DJ Arnot and TN Lambert, ACS APPLIED POLYMER MATERIALS, 4, 2470-2480 (2022).

DOI: 10.1021/acsapm.1c01798

In alkaline zinc-manganese dioxide batteries, there is a need for selective polymeric separators that have good hydroxide ion conductivity but that prevent the transport of zincate (Zn(OH)(4))(2-). Here we investigate the nanoscale structure and hydroxide transport in two cationic polysulfones that are promising for these separators. We present the synthesis and characterization for a tetraethylammonium- functionalized polysulfone (TEA-PSU) and compare it to our previous work on an N-butylimidazolium-functionalized polysulfone (NBI-PSU). We perform atomistic molecular dynamics (MD) simulations of both polymers at experimentally relevant water contents. The MD simulations show that both polymers develop well phase separated nanoscale water domains that percolate through the polymer. Calculation of the total scattering intensity from the MD simulations reveal weak or nonexistent ionomer peaks at low wave vectors. The lack of an ionomer peak is due to a loss of contrast in the scattering. The small water domains in both polymers, with median diameters on the order of 0.5-0.7 nm, lead to hydroxide and water diffusion constants that are 1-2 orders of magnitude smaller than their values in bulk water. This confinement lowers the conductivity but also may explain the strong exclusion of zincate from the PSU membranes seen experimentally.

Return to Publications page